Optimal Design and Experience for Fatigue Testing Clamp of Smooth Specimens
-
摘要: 高频疲劳实验机的夹具压盘上的螺纹容易损坏,严重时会导致工件无法取下。通过20MnTiB棒材在PLG-100高频疲劳试验机上进行疲劳实验时,多次借助扳手拧下试样而损坏了夹具压盘的螺纹,导致夹具压盘无法将试样固定在疲劳机上继续试验。针对此问题提出3种修复压盘螺纹的方法,分别在压盘中心镶嵌圆柱套、同心圆柱台阶套和螺纹套。疲劳试验结果表明:只有镶嵌螺纹套修复法能完成实验的要求并得到了疲劳寿命曲线水平部且维修方便,快速经济。与前两种方法比较,镶嵌螺纹套法能提高螺纹连接强度、耐热性和耐磨性。Abstract: The thread on the clamp pressure plate of high frequency fatigue test machine easily damaged, and which led to not remove the work-piece. In the fatigue test process of 20MnTiB bar under high frequency on the PLG-100 machine, the thread of the clamp pressure plate was damaged with the aid of a wrench repeatedly, and the work-piece was not fixed on the fatigue test machine. Then three methods to repair the pressure plate thread are presented, including embedded cylinder sleeve, sleeve of concentric cylindrical steps and the threaded sleeve in the center of the pressure plate. The fatigue test results indicated that with the repair method of threaded sleeve could complete the test requirement and the horizontal portion of fatigue life curve was obtained and convenient maintenance, rapid economy. Comparing the former two methods, the method inset threaded sleeve could improve the thread connection strength, heat resistance and abrasion resistance.
-
Key words:
- clamp pressure plate /
- fatigue life curve /
- fatigue test /
- pressure plate thread /
- threaded sleeve
-
[1] 李跃光,姬战国.国内高频疲劳试验机的技术现状及其发展[J].试验技术与试验机,2006,45(1):1-4 Li Y G, Ji Z G. The technical present situation and development of china's domestic high frequency fatigue testing machines[J]. Test Technology and Testing Machine, 2006,45(1):1-4 (in Chinese) [2] 郑铭章.PLG系列高频疲劳试验机[J].试验技术与试验机,1996,36(3-4):9-11 Zheng M Z. PLG series of high frequency fatigue testing machines[J]. Test Technology and Testing Machine, 1996,36(3-4):9-11 (in Chinese) [3] 宋欣,唐文明,沙宇,等.高频疲劳实验机薄板试件夹具研究[J].机械工程师,2009, (3):113-115 Song X, Tang W M, Sha Y, et al. Study of thin-plate specimen fixture of high-frequency fatigue testing machine[J]. Mechanical Engineer, 2009,(3):113-115 (in Chinese) [4] 黄小平,崔维成,张锦飞,等.板试件疲劳实验夹具设计及使用经验[J].实验室研究与探索,2003,22(6):98-101 Huang X P, Cui W C, Zhang J F, et al. Design and using experience of the fatigue testing clamp for plate specimens[J]. Research and Exploration in Laboratory, 2003,22(6):98-101 (in Chinese) [5] 王胜辉,陈进,吴益文.小试样的疲劳实验及其夹具设计[J].理化检验:物理分册,2009,45(4):246-247 Wang S H, Chen J, Wu Y W. Fatigue test and clamping design of small specimen[J]. Physical Testing and Chemical Analysis (Part: A Physical Testing), 2009,45(4):246-247 (in Chinese) [6] 米亦农.国外内高频疲劳试验机的发展状况[J].试验技术与试验机,1980,(3):1-13 Mi Y N. The development of international high frequency fatigue testing machines[J]. Material Testing Machine, 1980,19(3):1-13 (in Chinese) [7] 王学智,李春明.我国试验机标准化工作的回顾与展望[J].试验技术与试验机,2006,46(3):69-77 Wang X Z, Li C M. Review and prospect of the National standardization of testing machines in China[J]. Test Technology and Testing Machine, 2006,46(3):69-77 (in Chinese) [8] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.GB/T3075-2008 金属材料 疲劳试验 轴向力控制方法[S].北京:中国标准出版社,2008 AQSIQ, SAC. GB/T3075-2008 Metallic materials-Fatigue testing-Axial-force-controlled method[S]. Beijing: Standards Press of China, 2008 (in Chinese) [9] 赵少汴.抗疲劳设计[M].北京:机械工业出版社,1994 Zhao S B. Anti-fatigue design[M]. Beijing: China Machine Press, 1994 (in Chinese) [10] 张继旺,鲁连涛,张艳斌,等.疲劳极限小样本评估方法[J].哈尔滨工程大学学报,2010,31(3):336-339 Zhang J W, Lu L T, Zhang Y B, et al. Evaluating fatigue limits with Small data samples[J]. Journal of Harbin Engineering University, 2010,31(3):336-339 (in Chinese) [11] 石长伟,刘志明.小样本评估方法[J].质量与可靠性,2006,(6):24-26 Shi C W, Liu X M. Evaluting with small data samples[J]. Quality and Reliability, 2006,(6):24-26 (in Chinese) [12] 周利东,温玉全,王玮,等.引信可靠性小样本评估方法研究[J].北京理工大学学报,2010,30(7):761-764,770 Zhou L D, Wen Y Q, Wang W, et al. Method of fuse reliability evaluation based on small size of sample[J]. Transaction of Beijing Institute of Technology, 2010,30(7):761-764,770 (in Chinese) [13] Silva F S. The importance of compressive stresses on fatigue crack propagation rate[J]. International Journal of Fatigue, 2005,27(10-12):1441-1452 [14] 杨务滋,杨国庆,杨超,等.焊接中残余应力的大小与分布及减少措施[J].上海有色金属,2003,24(4):152-155,165 Yang W Z, Yang G Q, Yang C, et al. Magnitude and distribution of residual stress and methods for reducing them during welding[J]. Shanghai Nonferrous Metals, 2003,24(4):152-155,165 (in Chinese) [15] 罗利伟,付小超.焊接残余应力的产生及其消除方法[J].山西建筑,2008,34(20):134-135 Luo L W, Fu X C. Generation and erase method of residual stress by welding[J]. Shanxi Architecture, 2008,34(20):134-135 (in Chinese)
点击查看大图
计量
- 文章访问数: 186
- HTML全文浏览量: 35
- PDF下载量: 7
- 被引次数: 0