Comparative Study on Corrosion Behavior of 7B04 Aluminum Alloy Riveted Structure under Different Sea Areas
-
摘要: 在两种不同海域的海洋环境下对7B04铝合金铆接结构试验件进行自然曝晒,通过对试验件一年后腐蚀情况的对比分析,研究了这两种海洋服役环境对7B04铝合金的腐蚀影响。结果表明:两种海域的海洋环境对7B04铝合金铆接结构试验件都产生了明显的腐蚀行为,疲劳性能均有不同程度的下降,涂层对海洋环境能够起到较好的防护作用;同时两种海洋环境对7B04铝合金腐蚀行为的影响也表现出明显的差异性,必须对更严酷的服役环境做好针对性的腐蚀防护工作。Abstract: 7B04 aluminum alloy riveted structure specimens were exposured in two different marine environments for one year. The corrosion of the specimens was comparatively analyzed, and the effect of the two service environments on the corrosion behavior of 7B04 aluminum alloy was studied. The results show that the corrosion of 7B04 aluminum alloy riveted structure specimens has occurred obviously in the two marine environments, the fatigue performance of specimens has been reduced with varying degree. But coatings can protect the aluminum alloy away from destruction in marine environment. The effect of the two marine environments on the corrosion behavior of 7B04 aluminum alloy also shows obvious difference, the corrosion protection must be done well in service environment.
-
Key words:
- aluminum alloy /
- corrosion behavior /
- fatigue property
-
表 1 试验件数量及分类
试验件编号 试件类型 试验环境 类别名称 L-1~L-5 裸件 舰艇服役海域 L1类试件 M-1~M-5 涂层 舰艇服役海域 M1类验件 L-6~L-10 裸件 小麦岛 L2类试件 M-6~M-10 涂层 小麦岛 M2类试件 L-11~L-15 裸件 无 L3类试件 表 2 L1与L2类试验件腐蚀情况统计
试验环境 小麦岛 舰艇服役海域 平均腐蚀坑数目/个 1.5 3.2 平均腐蚀坑深度/μm 14.799 17.452 平均腐蚀坑宽度/μm 6.918 8.336 表 3 L3类试验件疲劳寿命
试件编号 最大应力/MPa 疲劳寿命/次 寿命均值/次 L-11 91.32 137255 188541 L-12 85.54 215468 L-13 106.27 98542 L-14 85.54 294571 L-15 102.32 196873 表 4 试验件疲劳寿命
试件分类 试件编号 疲劳寿命/次 平均寿命/次 L1 L-1 6182 4660 L-2 5423 L-3 7292 L-4 2811 L-5 1592 L2 L-6 35627 63100 L-7 66945 L-8 100226 L-9 46810 L-10 65894 M1 M-1 13284 11677 M-2 22314 M-3 9652 M-4 4574 M-5 8562 M2 M-6 84251 71844 M-7 58941 M-8 94851 M-9 65339 M-10 55842 -
[1] 齐忠原, 巫瑞智, 王国军, 等. 铝合金在船舶和海洋工程中的应用[J]. 轻合金加工技术, 2016, 44(1): 12-18Qi Z Y, Wu R Z, Wang G J, et al. Application of aluminum alloys in shipping and ocean engineering[J]. Light Alloy Fabrication Technology, 2016, 44(1): 12-18 (in Chinese) [2] 侯健, 张彭辉, 郭为民. 船用铝合金在海洋环境中的腐蚀研究[J]. 装备环境工程, 2015, 12(2): 59-63, 80Hou J, Zhang P H, Guo W M. Study on corrosion of aluminum alloys for ship applications in marine environment[J]. Equipment Environmental Engineering, 2015, 12(2): 59-63, 80 (in Chinese) [3] Han B, Tao W, Chen Y B, et al. Double-sided laser beam welded T-joints for aluminum-lithium alloy aircraft fuselage panels: Effects of filler elements on microstructure and mechanical properties[J]. Optics & Laser Technology, 2017, 93: 99-108 [4] 刘治国, 颜光耀, 吕航. 7B04铝合金服役环境下点蚀表面损伤特征研究[J]. 环境技术, 2017, 35(5): 46-49, 64 doi: 10.3969/j.issn.1004-7204.2017.05.014Liu Z G, Yan G Y, Lv H. Research on pitting corrosion damage characteristics of 7B04 aluminum alloys in service environment[J]. Environmental Technology, 2017, 35(5): 46-49, 64 (in Chinese) doi: 10.3969/j.issn.1004-7204.2017.05.014 [5] Sabelkin V, Mall S, Misak H. Investigation into corrosion pit-to-fatigue crack transition in 7075-T6 aluminum alloy[J]. Journal of Materials Engineering and Performance, 2017, 26(6): 2535-2541 doi: 10.1007/s11665-017-2697-4 [6] Feng L B, Yan Z N, Qiang X H, et al. Facile formation of superhydrophobic aluminum alloy surface and corrosion-resistant behavior[J]. Applied Physics A, 2016, 122(3): 165 doi: 10.1007/s00339-016-9700-z [7] 孙祚东. 军用飞机典型铝合金结构腐蚀损伤规律及加速腐蚀试验方法研究[D]. 哈尔滨: 哈尔滨工程大学, 2005Sun Z D. Study on corrosion damage of the typical aluminum alloy of air force plane and the test of accelerated corrosion[D]. Harbin: Harbin Engineering University, 2005 (in Chinese) [8] 孙飞龙, 李晓刚, 卢琳, 等. 5052和6061铝合金在中国南海深海环境下的腐蚀行为研究[J]. 金属学报, 2013, 49(10): 1219-1226 doi: 10.3724/SP.J.1037.2013.00143Sun F L, Li X G, Lu L, et al. Corrosion behavior of 5052 and 6061 aluminum alloys in deep ocean environment of South China Sea[J]. Acta Metallurgica Sinica, 2013, 49(10): 1219-1226 (in Chinese) doi: 10.3724/SP.J.1037.2013.00143 [9] 刘二勇, 曾志翔, 赵文杰. 海水环境中金属材料腐蚀磨损及耐磨防腐一体化技术的研究进展[J]. 表面技术, 2017, 46(11): 149-157Liu E Y, Zeng Z X, Zhao W J. Corrosive wear and integrated anti-wear & anti-corrosion technology metallic materials in seawater[J]. Surface Technology, 2017, 46(11): 149-157 (in Chinese) [10] 中国航空工业总公司. HB 5287-96 金属材料轴向加载疲劳试验方法[S]. 北京: 中国航空工业总公司, 1996Aviation Industry Corporation of China. HB 5287-96 Fatigue test method for metal materials under axial loading[S]. Beijing: Aviation Industry Corporation of China, 1996 (in Chinese) [11] 苏艳. 7B04高强铝合金与防护涂层在海洋大气环境中的腐蚀行为[D]. 重庆: 重庆大学, 2011Su Y. Corrosion behavior research of 7B04 high-strength aluminum alloy and its protective coating in marine atmospheric environment[D]. Chongqing: Chongqing University, 2011 (in Chinese) [12] 张洋洋, 上官晓峰. 7050铝合金盐雾腐蚀疲劳性能的研究[J]. 西安工业大学学报, 2014, 34(10): 845-850 doi: 10.3969/j.issn.1673-9965.2014.10.018Zhang Y Y, Shangguan X F. Research on fatigue performance of 7050 aluminum alloy in salt fog corrosion[J]. Journal of Xi' an Technological University, 2014, 34(10): 845-850 (in Chinese) doi: 10.3969/j.issn.1673-9965.2014.10.018 [13] 李令芳. 民机结构耐久性与损伤容限设计手册: 疲劳设计与分析[M]. 北京: 航空工业出版社, 2003Li L F. Civil aircraft structure durability and damage tolerance design manual: fatigue design and analysis[M]. Beijing: Aviation Industry Press, 2003 (in Chinese) [14] Di Cicco F, Fanelli P, Vivio F. Fatigue reliability evaluation of riveted lap joints using a new rivet element and DFR[J]. International Journal of Fatigue, 2017, 101: 430-438 doi: 10.1016/j.ijfatigue.2017.02.006