Reliability Analysis of Fatigue Crack Growth Life of QT400-18
-
摘要: 采用概率断裂力学方法研究了船用柴油机机身球墨铸铁材料(QT400-18)的裂纹扩展寿命可靠性。基于QT400-18的裂纹扩展试验,考虑了裂纹扩展速率的分散性,采用统计分析获得了Paris公式参数的分布特征,建立了QT400-18裂纹扩展速率的随机概率模型。反推得到了da/dN≤10-7 mm/cycle时材料的疲劳启裂门槛值。进一步建立了剩余寿命预测模型,通过数值抽样仿真,得到了不同初始裂纹长度下的裂纹扩展剩余寿命及其分布,并建立了剩余寿命与可靠度关系图谱。Abstract: This paper investigated the reliability evaluation process of crack propagation life of marine diesel engine body material QT400-18 with probabilistic fracture mechanics method. Based on the crack propagation experiments of QT400-18 and considering the dispersion of crack propagation rate, we obtain the Paris formula parameters with statistical analysis, and establish a random probability model of crack propagation rate of QT400-18. Furthermore, a residual life reliability prediction model is also built. Through the numerical sampling simulation, the residual life and its distribution in different initial crack length are achieved and the correlation curve of reliability with residual life is drawn. In the condition of, the threshold of fatigue crack growth is obtained with an inversion approach.
-
Key words:
- crack initiation /
- crack propagation rate /
- crack tips /
- diesel engines
-
[1] Noroozi A H, Glinka G, Lambert S. A study of the stress ratio effects on fatigue crack growth using the unified two-parameter fatigue crack growth driving force[J]. International Journal of Fatigue,2007,29:1616-1633 [2] 冯蕴雯,应中伟,薛小锋,等.基于多裂纹扩展随机模型估算疲劳寿命的方法研究[J]. 西北工业大学学报,2008,4(26):436-440 Feng Y W, Ying Z W, Xue X F, et al. A new method for computing fatigue life based on stochastic modeling of multi-crack propagation[J]. Journal of Northwestern Poly technical University,2008,4(26):436-440 (in Chinese) [3] 周昌玉.疲劳裂纹扩展速率的统计分析及疲劳寿命的概率预测[J].南京化工大学学报,1999,(1):58-60 Zhou C Y. Statistial analysis of fatigue crack growth rate and probabilistical prediction of fatigue life time[J]. Journal of Nanjing University of Chemical Technology,1999,(1):58-60 (in Chinese) [4] Kim S J, Jeong Y H, Sohn H J. Probabilistic fatigue crack growth in compact tension specimens from FSWed 7075-T651 aluminum alloys[J]. Mechanical Engineer and Materials,2012,(1):293-296 [5] 王坤茜,徐人平,林捷晖.考虑应力比的疲劳裂纹扩展概率模型[J].航空动力学报,2009,24(9):2012-2017 Wang K Q, Xu R P, Lin J H. Fatigue crack growth probability model based on stress ratio[J]. Journal of Aerospace Power,2009,24(9):2012-2017 (in Chinese) [6] Kocanda D, Jasztal M. Probabilistic prediction the fatigue crack growth under variable amplitude loading[J]. International Journal of Fatigue,2012,39:68-74 [7] 熊峻江,彭俊华,高镇同.断裂韧性KIC和断裂门槛值ΔKth可靠性测定方法[J].北京航空航天大学学报,2000,26(6):694-696 Xiong J J, Peng J H, Gao Z T. Reliability methods to determine fracture toughness KIC and fracture threshold value ΔKth[J]. Journal of Beijing University of Aeronautics and Astronautics,2000,26(6):694-696 (in Chinese) [8] GB/T6398-2000.金属材料疲劳裂纹扩展速率试验方法[S].北京:中国标准出版社,2000 GB/T6398-2000. Standard test method for fatigue crack growth rates of metallic materials[S]. Beijing:Standards Press of China,2000 (in Chinese) [9] Bergner F, Zouhar G. A new approach to the correlation between the coefficient and the exponent in the power law equation of fatigue crack growth[J]. International Journal of Fatigue,2000,22:229-239 [10] 田秀云,杜洪增,孙智强.金属材料疲劳裂纹扩展速率曲线的拟合方法研究[J].工程力学,2003,20(4):136-140 Tian X Y, Du H Z, Sun Z Q. Curve fitting of the fatigue crack growth characterristic of metals[J]. Engineering Mechanics,2003,20(4):136-140 (in Chinese) [11] 刘媛,吕运冰,黄婧.疲劳裂纹扩展公式中的材料常数的统计相关性及疲劳扩展寿命预测[J].武汉理工大学学报,2004,28(6):870-872 Liu Y, Lü Y B, Huang J. Statistical correlation of material coefficient in fatigue cracks propagation formula and prognosticating propagation life of fatigue[J]. Journal of Wuhan University of Technology,2004,28(6):870-872 (in Chinese) [12] 方灿,陈国明.模糊概率断裂力学[M].东营:中国石油大学出版社,1999 Fang C, Cheng G M. Fuzzy probabilistic fracture mechanics[M]. Dongying:China University of Petroleum Press,1999 (in Chinese) [13] Liu J Z, Wu X R, Ding C F, et al. Crack growth behavior and fatigue life prediction based on worst case near threshold data of large crack for 9310 steel[J]. Fatigue & Fracture of Engineering Materials & Structure,2002,25:467-280 [14] 高宗战,刘伟,岳珠峰,等.有机玻璃疲劳裂纹扩展[J].材料科学与工程学报,2008,26(1):90-93 Gao Z Z, Liu W, Yue Z F, et al. Fatigue crack propagation in polyethylene methacrylate[J]. Journal of Materials Science and Engineering,2008,26(1):90-93 (in Chinese) [15] 刘文挺.疲劳裂纹门槛值试验的可靠性分析[J].实验力学,1987,2(4):39-46 Liu W T. The reliability analysis of fatigue crack growth threshold test[J]. Journal of Experimental Mechanics,1987,2(4):39-46 (in Chinese)
点击查看大图
计量
- 文章访问数: 180
- HTML全文浏览量: 29
- PDF下载量: 5
- 被引次数: 0