三维打印技术工艺参数对制件表面形貌的影响

曹珊 李淑娟

曹珊, 李淑娟. 三维打印技术工艺参数对制件表面形貌的影响[J]. 机械科学与技术, 2012, 31(7): 1079-1084.
引用本文: 曹珊, 李淑娟. 三维打印技术工艺参数对制件表面形貌的影响[J]. 机械科学与技术, 2012, 31(7): 1079-1084.
Cao Shan, Li Shu-juan. The Influence of 3DP Processing Parameters on the Parts' Surfact Topography[J]. Mechanical Science and Technology for Aerospace Engineering, 2012, 31(7): 1079-1084.
Citation: Cao Shan, Li Shu-juan. The Influence of 3DP Processing Parameters on the Parts' Surfact Topography[J]. Mechanical Science and Technology for Aerospace Engineering, 2012, 31(7): 1079-1084.

三维打印技术工艺参数对制件表面形貌的影响

基金项目: 

国家973项目(2009CB724406)

陕西省工业攻关项目(2012K07-25)资助

详细信息
    作者简介:

    曹珊(1984-),硕士研究生,研究方向为机械制造,yetikss@qq.com;李淑娟(联系人),教授,博士生导师,shujuanli2009@gmail.com

    曹珊(1984-),硕士研究生,研究方向为机械制造,yetikss@qq.com;李淑娟(联系人),教授,博士生导师,shujuanli2009@gmail.com

The Influence of 3DP Processing Parameters on the Parts' Surfact Topography

  • 摘要: 三维打印技术(three dimension printing,3DP)作为一种重要的固体无模成型(solid free formfabrication,SFF)方法以其成型速度快、无环境污染、可制作材料多而得到快速的发展和应用。本文以ZP310三维打印机为实验平台,研究制件的放置位置、铺粉层厚以及饱和度水平等打印参数对制件表面微观形貌和精度的影响。采用全因子实验方法,获得不同打印参数下的长方体制件,然后使用三维轮廓仪测量制件的表面形貌。结果表明:对于使用ZP130粉末制造的制件,铺粉层厚为0.1 mm饱和度为70%在制造室左侧放置时获得的制件表面形貌最好。
  • [1] Turker M,Godlinski D.Effect of production parameters on the properties of IN718superalloy by three-dimensional printing[J].Materials Characterrization,2008,59:1728~1735
    [2] Lu K,Reynolds W T.3DP process for fine mesh structure print-ing[J].Powder Technology,2008,187:11~18
    [3] Lam C X F,Mo X M.Scaffold development using3D printing with a starch-based polymer[J].Materials Science and Engi-neering,2002,C20:49~56
    [4] Williams C B,Cochran J K.Additive manufacturing of metallic cellular materials via three-dimensional printing[J].The Inter-national Journal of Advanced Manufacturing Technology,2011,53:231~239
    [5] Lu K,Hiser M,Wu W.Effect of particle size on three dimen-sional printed mesh structures[J].Powder Technology,2009,192:178~183
    [6] Vaezi M,Chua C K.Effects of layer thickness and binder satura-tion level parameters on3D printing process[J].The Interna-tional Journal of Advanced Manufacturing Technology,2010,53:275~284
    [7] Suwanprateeb J.Improvement in mechanical properties of three-dimensional printing parts made from natural polymers reinforced by acrylate resin for biomedical applications:a double infiltration approach[J].Polymer International,2006,55:57~62
    [8] 李晓燕,张署,余灯广.三维打印成形粉末配方的优化设计[J].机械科学与技术,2006,25(11):1343~1346
    [9] 李晓燕,张署.3DP成形技术的机理研究及过程优化[D].同济大学,2006
    [10] 刘厚才,莫健华,刘海涛.三维打印快速成型技术极其应用[J].机械科学与技术,2008,22(9):1184~1186
    [11] Utela B,Storti D,Anderson R.A review of process development steps for new material systems in three dimensional printing(3DP)[J].Journal of Manufacturing Processes,2008,10:96~104
    [12] 周密,李淑娟.基于逆向工程的曲面加工及快速制造技术研究[D].西安理工大学,2007
  • 加载中
计量
  • 文章访问数:  153
  • HTML全文浏览量:  25
  • PDF下载量:  5
  • 被引次数: 0
出版历程
  • 收稿日期:  2011-05-30
  • 刊出日期:  2015-06-10

目录

    /

    返回文章
    返回