金属微滴形成过程图像采集及关键参数测量

肖渊; 齐乐华; 罗俊; 钟宋义; 周计明

金属微滴形成过程图像采集及关键参数测量

肖渊^1,3,
齐乐华^1,2,
罗俊¹,
钟宋义¹,
周计明¹

1.
西北工业大学机电学院,西安 710072;
2.
西安工程大学机电工程学院,西安 710048;
3.
西北工业大学现代设计与集成制造技术教育部重点实验室,西安 710072

基金项目:

国家高技术研究发展计划项目(863计划,2008AA03A238)

国家自然科学基金项目(51005186)

优秀博士论文作者专项基金项目(2007B3)资助

详细信息

作者简介:
肖渊(1975-)，博士研究生，研究方向为机械制造及其自动化，计算机测控技术，xiaoyuanjidian@mail.nwpu.edu.cn;齐乐华(联系人)，教授，博士生导师，qileliua@nwpu.edu.cn

肖渊(1975-)，博士研究生，研究方向为机械制造及其自动化，计算机测控技术，xiaoyuanjidian@mail.nwpu.edu.cn;齐乐华(联系人)，教授，博士生导师，qileliua@nwpu.edu.cn

计量
- 文章访问数: 442
- HTML全文浏览量: 29
- PDF下载量: 12
- 被引次数: 0
出版历程
- 收稿日期: 2011-08-22
- 刊出日期: 2015-06-10

Acquisition the Image and Measurement of Key Parameters in Metal Droplet Forming Process

1.
School of Mechatronic,Northwestern Polytechnical University,Xi'an 710072;
2.
Education Ministry Key Laboratory of Modern Design and Integrated Manufacturing Technology, Northwestern Polytechnical University,Xi'an 710072;
3.
School of Mechanical and Electrical Engineering,Xi'an Polytechnic University,Xi'an 710048

摘要

摘要: 针对气压驱动金属微滴按需喷射系统产生的微滴尺寸较小、断裂过程持续时间短,其关键参数不易直接测量的问题,构建了基于延时触发的金属微滴喷射过程图像采集系统。使用直径为200μm喷嘴,在系统稳定喷射情况下,对锡铅合金(60%Sn～40%Pb)微滴的形成和喷射过程进行图像采集、机理分析及关键参数测量研究。实验结果表明:通过将不同延时时刻的采集图像进行组合,可以再现按需喷射系统微滴形成的动态过程及其形态变化;测得了各时刻微滴的位置坐标和直径,计算出微滴平均飞行速度和喷射方向;揭示了金属微滴成形机理和随着飞行距离增大,微滴发散愈剧烈的变化趋势。
- 按需喷射 /
- 快速原型 /
- 均匀微滴 /
- 速度测量
Abstract: It is difficult to directly measure the key parameters of metal droplets during the spraying process,because the size of metal droplet is small and the rupture process is short duration based on the principle of pneumatic drop-on-demand generation.In order to solve this problem,the image acquisition system for the metal droplet forming process was constructed based on delay trigger method.Sn-Pb alloy(60%Sn～40%Pb) droplet spray experiments had been conducted with a generator nozzle of 200 μm in diameter.The steady spray process was captured by the image acquisition system,then the forming mechanism of the metal droplet was analyzed and the key parameters were measured.The results show that the spraying process of metal droplet can be reappeared by combining different photographs of delay time.The coordinates and diameter of droplets were obtained in different delay times,and the flight velocity and deviation angle of droplets were calculated.The generating mechanic of metal droplets was revealed,and the change trends of droplet divergent was predicted along with the increasing of flight distance.
- drop-on-demand /
- rapid prototyping /
- uniform droplet /
- droplet speed measurement

HTML全文

参考文献(13)

[1]	Cao W B,Miyamoto Y. Freeform fabrication of aluminum parts by direct deposition of molten aluminum[J].Journal of Mate-rials Processing Technology,2006,(02):209-212.
[2]	Chun J H,Passow C H. Droplet-based manufacturing[J].An-nals of the CIRP,1993,(01):235-238.
[3]	朱玉芳,杨继全,岳东. 多材料模型的数字化喷射成型方法[J].机械科学与技术,2009,(02):200-204.
[4]	Cheng S. A pneumatic droplet-on-demand generator[J].Experiments in Fluids,2003,(6):755-762.
[5]	Fang M,Chandra S,Park C B. Experiments on remelting and solidification of molten metal droplets deposited in vertical col-umns[J].Journal of Manufacturing Science and Engineer-ing,2007.311-319.
[6]	李杨,齐乐华,罗俊. 金属熔滴气动按需喷射特性试验研究[J].西安交通大学学报,2011,(05):69-73.
[7]	Kwon K S. Speed measurement of ink droplet by using edge de-tection techniques[J].Measurement,2009.44-50.
[8]	罗海燕,翟超,金熠. 光电系统检测回转误差的实验研究[J].仪器仪表学报,2008,(10):2141-2145.
[9]	杨观,齐乐华,罗俊. 均匀液滴喷射成形中微熔滴关键参数在线检测系统[J].仪器仪表学报,2009,(03):590-595.
[10]	Hsing P C,Tankin R S. Measurement of droplet size,velocity,and temperature distributions in rayleigh flow[J].Experiments in Fluids,1996,(02):144-152.
[11]	Cheng X,Li T G,Chandra S. Producing molten metal droplets with a pneumatic droplet-on-demand generator[J].Journal of Materials Processing Technology,2005,(159):295-302.
[12]	魏大忠,张人估,吴人东. 压电驱动微滴喷射过程的数学模型[J].中国机械工程,2005,(07):611-614.
[13]	李京龙,李长久. 等离子喷涂熔滴与基体的相互作用机理研究[J].机械科学与技术,2000,(01):88-90,99.