辉光离子渗氮对Ti6Al4V合金在航空煤油中摩擦学性能的影响

汤金钢; 刘道新; 唐长斌; 张晓化; 熊华; 唐宾

辉光离子渗氮对Ti6Al4V合金在航空煤油中摩擦学性能的影响

1.
西北工业大学腐蚀与防护研究所, 西安 710072;
2.
西安建筑科技大学, 西安 710055;
3.
西安航空动力控制科技有限公司, 西安 710077;
4.
太原理工大学表面工程研究所, 太原 030024

基金项目:

国家自然科学基金项目(51171154,51101127)资助

详细信息

作者简介:
汤金钢(1983-)，博士研究生，研究方向为材料损伤与修复和腐蚀与防护技术，jingangtang@163.com;刘道新(联系人)，教授，博士生导师，liudaox@nwpu.edu.cn

汤金钢(1983-)，博士研究生，研究方向为材料损伤与修复和腐蚀与防护技术，jingangtang@163.com;刘道新(联系人)，教授，博士生导师，liudaox@nwpu.edu.cn

计量
- 文章访问数: 148
- HTML全文浏览量: 28
- PDF下载量: 7
- 被引次数: 0
出版历程
- 收稿日期: 2012-08-23
- 刊出日期: 2015-06-10

The Effect of the Plasma Nitriding Layer in Aviation Kerosene Environment on the Tribological Behavior of Ti6Al4V Titanium Alloy

1.
Corrosion and Protection Research Institute, Northwestern Polytechnical University, Xi'an 710072;
2.
Xi'an University of Architecture and Technology, Xi'an 710055;
3.
Xi'an Aviation Power Control Technology Limited Company, Xi'an 710077;
4.
Institute of surface engineering, Taiyuan University of Technology, Taiyuan 030024

摘要

摘要: 为改善钛合金在航空煤油中的摩擦学性能,采用辉光离子渗氮技术对Ti6Al4V钛合金表面进行改性处理。分析了渗氮层的表面形态、组织结构、显微硬度沿层深的分布,对比研究了钛合金基体、渗氮层和5CrMnMo工具钢在航空煤油中分别与GCr15钢及QSn4-3铜合金配副对磨时的耐磨性能,并探讨了渗氮层的表面粗糙度对摩擦磨损行为的影响。结果表明:Ti6Al4V钛合金表面渗氮层硬度明显高于5CrMnMo工具钢,经表面抛光后处理,其耐磨性能显著优于钛合金基材与5CrMnMo工具钢,同时也有效降低了摩擦配副的表面磨损。研究同时发现QSn4-3铜合金配副的磨损体积损失与渗氮层的表面粗糙度呈线性递增关系,原因归于铜合金配副的磨损失效由渗氮层表面微凸体的磨粒磨损作用及航空煤油的润滑状况决定。
- 离子渗氮 /
- Ti6Al4V合金 /
- 磨损 /
- 航空煤油
Abstract: In order to improve the tribological behavior in aviation kerosene, plasma nitriding layer in the Ti6Al4Vbase alloy were fabricated by using a plasma glow-discharge surface technique. The morphology, microstructure and microhardness depth distribution of the plasma nitriding layer were studied. The tribological properties of the Ti6Al4Vbase alloy, nitriding layer and 5CrMnMo steel sliding with GCr15 steel or QSn4-3 copper alloy counterparts in aviation kerosene were comparatively studied. The effect of the roughness on the sliding wear behavior was discussed. The re-sults indicated that the nitriding modified layer with polishing treatment not only reduce the wear volume of Ti6Al4Vbase alloy, but also enhance the wear resistance of the counterparts due to the high microhardness of nitriding layer.The nitriding modified layer has better tribological behavior than that of 5CrMnMo steel. It is also found that the wear volume loss of the counterparts is proportional to the value of roughness of nitriding modified layer, which is related directly to the ploughing wear between micro convex bodies of the layer and counterparts.
- copper alloys /
- kerosene /
- microhardness /
- morphology

HTML全文

参考文献(15)

[1]	Slatter T,Taylor H,Lewis R,et al.The influence of laser hardening on wear in the valve and valve seat contact[J].Wear,2009,267:797-806
[2]	Peter G,Joh C S.Wear in check valves due to flow induced motion[J].Nuclear Engineering and Design,2003,115(2-3):323-330
[3]	Carrera E,Rodrguez A,Talamantes J.Measurement of residual stresses in cast aluminium engine blocks[J].Journal of Materials Processing Technology,2007,189:206-210
[4]	Gurrappa I.An oxidation model for predicting the life of titanium alloy components in gas turbine engines[J].Journal of Alloys and Compounds,2005,389:190-197
[5]	Yildiz F,Yetim A F,Alsaran A,et al.Wear and corrosion behaviour of various surface treated medical grade titanium alloy in bio-simulated environment[J].Wear,2009,267:695-701
[6]	Nolan D,Huang S W,Leskovsek V,et al.Sliding wear of titanium nitride thin films deposited on Ti-6Al-4V alloy by PVD and plasma nitriding processes[J].Surface and Coatings Technology,2006,200:5698-5705
[7]	Fan W D,Jagannadham K,Narayan J.Adhesion of diamond films on Ti-6Al-4V alloys[J].Surface and Coatings Technology,1997,91:32-36
[8]	Vásqueza V Z,Ozcan M,Kimpara E T.Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloy after thermal-and mechanical-loading[J].Dental Materials,2009,25(2):221-231
[9]	Xu Z,Liu X,Zhang P.Double glow plasma surface alloying and plasma nitriding[J].Surface and Coatings Technology,2007,201:4822-4825
[10]	Zhecheva A,Shaa W,Malinov S,et al.Enhancing the microstructure and properties of titanium alloys through nitriding and other surface engineering methods[J].Surface and Coatings Technology,2005,200:2192-2207
[11]	刘道新,陈华,何家文.等离子渗氮与喷丸强化复合改进钛合金抗微动损伤性能[J].材料热处理学报,2001,22(3):49-54Liu D X,Chen H,He J W.The effect of plasma nitriding and shot peening on the fretting damage resistance of Ti alloy[J].Transactions of Materials Heat Treatment,2001,22(3):49-54(in Chinese)
[12]	刘国华,刘道新,张晓化,等.Cu/Ni多层膜在多冲与压压载荷下的失效行为[J].中国表面工程,2009,22(2):31-36Liu G H,Liu D X,Zhang X H,et al.Failure behavior of Cu/Ni multilayer under multiple impacting and repeating press load[J].China Surface Engineering,2009,22(2):31-36(in Chinese)
[13]	Zhang S,Sun D,Fu Y Q.Toughness measurement of thin films:a critical review[J].Surface and Coatings Technology,2005,198:74-84
[14]	Luo J B,Liu S.The investigation of contact ratio in mixed lubrication[J].Tribology International,2006,39:409-416
[15]	温诗铸,黄平.摩擦学原理[M].北京:清华大学出版社,2002Wen S Z,Huang P.Tribology theory[M].Beijing:Tsinghua University Press,2002(in Chinese)