熔融沉积成形件的表面雾化抛光实验研究

张江涛 胡中伟 朱泽朋 张志斌

张江涛, 胡中伟, 朱泽朋, 张志斌. 熔融沉积成形件的表面雾化抛光实验研究[J]. 机械科学与技术, 2017, 36(6): 960-964. doi: 10.13433/j.cnki.1003-8728.2017.0623
引用本文: 张江涛, 胡中伟, 朱泽朋, 张志斌. 熔融沉积成形件的表面雾化抛光实验研究[J]. 机械科学与技术, 2017, 36(6): 960-964. doi: 10.13433/j.cnki.1003-8728.2017.0623
Zhang Jiangtao, Hu Zhongwei, Zhu Zepeng, Zhang Zhibin. Experimental Studies on Spray Polishing Surface of Fused Deposition Modeling Build Parts[J]. Mechanical Science and Technology for Aerospace Engineering, 2017, 36(6): 960-964. doi: 10.13433/j.cnki.1003-8728.2017.0623
Citation: Zhang Jiangtao, Hu Zhongwei, Zhu Zepeng, Zhang Zhibin. Experimental Studies on Spray Polishing Surface of Fused Deposition Modeling Build Parts[J]. Mechanical Science and Technology for Aerospace Engineering, 2017, 36(6): 960-964. doi: 10.13433/j.cnki.1003-8728.2017.0623

熔融沉积成形件的表面雾化抛光实验研究

doi: 10.13433/j.cnki.1003-8728.2017.0623
基金项目: 

国家自然科学青年基金项目(51205142)、华侨大学中青年教师科研提升计划项目(Z14J0009)及华侨大学研究生科研创新能力培育计划项目资助

详细信息
    作者简介:

    张江涛(1992-),硕士研究生,研究方向为增材制造,835710392@qq.com

    通讯作者:

    胡中伟(联系人),博士,讲师,硕士研究生导师,huzhongwei@hqu.edu.cn

Experimental Studies on Spray Polishing Surface of Fused Deposition Modeling Build Parts

  • 摘要: 针对熔融沉积成形(Fused deposition modeling,FDM)最常用的成形材料聚乳酸(Polylactic acid,PLA),选用氯仿溶液进行表面雾化抛光,以提高FDM成形件的表面质量。研究抛光温度、抛光时间和抛光液浓度对FDM成形件表面抛光效果的影响。实验结果表明抛光表面的粗糙度随着抛光温度升高和抛光时间增加而减小,但当抛光温度和抛光时间达到一定程度后,抛光表面粗糙度并没有明显的减小。随着抛光液浓度的增大,抛光表面的粗糙度减小。采用抛光温度为60℃、抛光时间为7 min和抛光液浓度为100%时的抛光效果较好,抛光后成形件的表面粗糙度大幅减小,表面形貌得到显著改善,且对成形件的尺寸和质量影响很小。
  • [1] 杰里米·里夫金, 张一萌. 第三次产业革命[J]. 国 际研究参考, 2013(6):31-34
    [2] Jeremy R, Zhang Y M. The third industrial revolution[J]. Internationalresearch Reference,2013(6):31-34 (in Chinese)
    [3] 于灏."中国制造2025"下的3D打印[J]. 新材料产业,2015(7):20-27
    [4] Yu H.3D Printing under "Made in China 2025"[J].Advanced Materials Industry,2015(7):20-27 (in Chinese)
    [5] Stephens B, Azimi P, El Orch Z, et al. Ultrafine particle emissions from desktop 3D printers[J]. Atmospheric Environment, 2013,79:334-339
    [6] Huang X M. Research on some key problems for fused deposition modeling[D]. Wuhan: Huazhong University of Science and Technology, 2009 (in Chinese)
    [7] Miller F P, Vandome A F, Mcbrewster J. Fused deposition modeling[J]. Architect, 2007,96(6):54
    [8] Chen X F, Rong J. Research of the quality of rapid prototyping based on FDM[J]. Journal of Suzhou Vocational University, 2009,20(1):17-19 (in Chinese)
    [9] Boparai K S, Singh R, Singh H. Development of rapid tooling using fused deposition modeling: a review[J]. Rapid Prototyping Journal, 2016,22(2):281-299
    [10] Zou G L, Jia Z Y, Gou D M, et al. Accuracy analysis and Taguchi experiment design of FDM technology[J]. Electromachining & Mould, 2001,(4):23-26 (in Chinese)
    [11] Sun Z J, Zhang X Y, Huang H, et al. Progress and application of solubility parameter[J]. China Rubber Industry, 2007,54(1):54-58 (in Chinese)
    [12] 黄小毛.熔丝沉积成形若干关键技术研究[D].武汉:华中科技大学,2009
    [13] Sheng S R, Song C S, Cai M Z. Determination of the solubility parameter of polyaryl ether sulfone ether ketone ketone containing naphthalene ring[J]. Engineering Plastics Application, 1999,27(5):22-24 (in Chinese)
    [14] Masood S H. Intelligent rapid prototyping with fused deposition modelling[J]. Rapid Prototyping Journal, 1996,2(1):24-33
    [15] Thrimurthulu K, Pandey P M, Reddy N V. Optimum part deposition orientation in fused deposition modeling[J]. International Journal of Machine Tools and Manufacture, 2004,44(6):585-594
    [16] Kumar M, Choudhury A R. Adaptive slicing with cubic patch approximation[J]. Rapid Prototyping Journal, 2002,8(4):224-232
    [17] 陈雪芳,荣静.基于FDM的快速成型质量的研究[J].苏州市职业大学学报,2009,20(1):17-19
    [18] Nancharaiah T, Raju D R, Raju V R. An experimental investigation on surface quality and dimensional accuracy of FDM components[J]. International Journal on Emerging Technologies, 2010,1(2):106-111
    [19] 邹国林,贾振元,郭东明,等.FDM工艺精度分析与正交试验设计[J].电加工与模具,2001,(4):23-26
    [20] Galantucci L M, Lavecchia F, Percoco G. Experimental study aiming to enhance the surface finish of fused deposition modeled parts[J]. CIRP Annals-Manufacturing Technology, 2009,58(1):189-192
    [21] Gajdoš I, Spišák E, Kaščák L, et al. Surface finish techniques for FDM parts[J]. Materials Science Forum, 2015,818:45-48
    [22] Drummer D, Cifuentes-Cuéllar S, Rietzel D. Suitability of PLA/TCP for fused deposition modeling[J]. Rapid Prototyping Journal, 2012,18(6):500-507
    [23] 孙志娟,张心亚,黄洪,等.溶解度参数的发展及应用[J].橡胶工业,2007,54(1):54-58
    [24] Tsuji H, Sumida K. Poly(L-lactide): V. effects of storage in swelling solvents on physical properties and structure of poly(L-lactide)[J]. Journal of Applied Polymer Science, 2001,79(9):1582-1589
    [25] 盛寿日,宋才生,蔡明中.含萘环聚醚砜醚酮酮的溶解度参数的测定[J].工程塑料应用,1999,27(5):22-24
  • 加载中
计量
  • 文章访问数:  195
  • HTML全文浏览量:  41
  • PDF下载量:  10
  • 被引次数: 0
出版历程
  • 收稿日期:  2016-08-16
  • 刊出日期:  2017-06-05

目录

    /

    返回文章
    返回